KKPC Kuhmo HI 410T Transparent HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Transparent Grade |
| Manufacturer | Korea Kumho Petrochemical Co., Ltd. |
| Trade Name | Kuhmo |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | KKPC Kuhmo HI 410T Transparent HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key features: Super high-gloss. Common Uses: Food container, transparent sheeting, tray, disposable cup, electronic parts packing.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-resistance and heat-resistance.Data provided by Korea Kumho Petrochemical Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 7.5 g/10 min | 7.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 39.6 MPa | 5750 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Yield Strength | 49.21 MPa | 7138 psi | ASTM D790 |
| Flexural Modulus | 1.909 GPa | 276.9 ksi | ASTM D790 |
| Izod Impact, Notched | 0.246 J/cm @Thickness 3.20 mm |
0.460 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | unannealed; ASTM D648 |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 2.20 mm |
HB @Thickness 0.0866 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Mfr species transparent but does not quantify |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ GPE3003-36 Natural Flame Retardant concentrate in Polyethylene
- Saint-Gobain Norton® V780 Medium-Density Pressure Sensitive Adhesive Sealant Foam
- Unitika M1030E PA6, Dry
- Formosa Plastics Formolene® 4100P Injection Molding Polypropylene
- Voloknohim Filament Nylon Linear Density 70 tex
- ExxonMobil LL 3003.32 Cast Film Resin
- Clariant ABS4500G30 ABS, 30% Glass Reinforced
- A. Schulman ComAlloy Lubrilon® 636 Nylon 6/6, Carbon Fiber Reinforced, Proprietary Lubricant Package
- Ferro CF 7570 Low-Temperature Sealing
Copyright © lookpolymers.com All Rights Reserved