Overview of materials for PVC, Molded

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for PVC, Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.550 - 2.50 g/cc
0.0199 - 0.0903 lb/in³
Average value: 1.29 g/cc Grade Count:568
Volatile Organic Compounds (VOC) Content 0.300 g/l
0.300 g/l
Average value: 0.300 g/l Grade Count:9
Apparent Bulk Density 0.470 - 0.780 g/cc
0.0170 - 0.0282 lb/in³
Average value: 0.549 g/cc Grade Count:11
Water Absorption 0.0200 - 0.400 %
0.0200 - 0.400 %
Average value: 0.260 % Grade Count:13
Particle Size 63.0 - 250 µm
63.0 - 250 µm
Average value: 157 µm Grade Count:12
Viscosity 0.680 - 2.27 cP
0.680 - 2.27 cP
Average value: 1.48 cP Grade Count:11
Viscosity Test 79.0 - 180 cm³/g
79.0 - 180 cm³/g
Average value: 121 cm³/g Grade Count:23
Thickness 1000 - 3000 microns
39.4 - 118 mil
Average value: 1100 microns Grade Count:26
Linear Mold Shrinkage 0.00100 - 0.0500 cm/cm
0.00100 - 0.0500 in/in
Average value: 0.00570 cm/cm Grade Count:30
Melt Flow 2.00 - 25.0 g/10 min
2.00 - 25.0 g/10 min
Average value: 13.4 g/10 min Grade Count:6
Spiral Flow 63.5 - 94.0 cm
25.0 - 37.0 in
Average value: 83.0 cm Grade Count:6
ASTM Color -32.4 - 97.2
-32.4 - 97.2
Average value: 18.7 Grade Count:58
Mechanical Properties Metric English Comments
Hardness, Shore A 28.0 - 99.0
28.0 - 99.0
Average value: 70.8 Grade Count:460
Hardness, Shore D 38.0 - 89.0
38.0 - 89.0
Average value: 72.0 Grade Count:61
Hardness, Shore C 75.0 - 95.0
75.0 - 95.0
Average value: 85.0 Grade Count:5
Tensile Strength, Ultimate 1.47 - 59.0 MPa
213 - 8560 psi
Average value: 16.6 MPa Grade Count:534
Tensile Strength, Yield 1.59 - 52.0 MPa
230 - 7540 psi
Average value: 14.2 MPa Grade Count:143
Elongation at Break 3.00 - 600 %
3.00 - 600 %
Average value: 309 % Grade Count:515
Modulus of Elasticity 0.00163 - 3.24 GPa
0.237 - 470 ksi
Average value: 2.12 GPa Grade Count:55
Flexural Yield Strength 2.83 - 103 MPa
410 - 15000 psi
Average value: 74.9 MPa Grade Count:45
Flexural Modulus 1.65 - 3.31 GPa
239 - 480 ksi
Average value: 2.66 GPa Grade Count:41
Izod Impact, Notched 0.214 - 28.4 J/cm
0.400 - 53.2 ft-lb/in
Average value: 6.21 J/cm Grade Count:42
0.534 - 7.47 J/cm

@Temperature -40.0 - 0.000 °C
1.00 - 14.0 ft-lb/in

@Temperature -40.0 - 32.0 °F
Average value: 3.11 J/cm Grade Count:4
0.534 - 7.47 J/cm

@Thickness 3.18 - 3.18 mm
1.00 - 14.0 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 3.11 J/cm Grade Count:4
Izod Impact, Unnotched 0.400 - 11.3 J/cm
0.749 - 21.3 ft-lb/in
Average value: 4.42 J/cm Grade Count:16
Tear Strength Test 145 - 530
145 - 530
Average value: 308 Grade Count:64
Tear Strength 15.0 - 55.0 kN/m
85.6 - 314 pli
Average value: 28.5 kN/m Grade Count:19
Thermal Properties Metric English Comments
CTE, linear 50.0 - 80.0 µm/m-°C
27.8 - 44.4 µin/in-°F
Average value: 55.4 µm/m-°C Grade Count:5
Maximum Service Temperature, Air 40.0 - 100 °C
104 - 212 °F
Average value: 52.4 °C Grade Count:30
Deflection Temperature at 0.46 MPa (66 psi) 66.0 - 90.6 °C
151 - 195 °F
Average value: 77.3 °C Grade Count:18
Deflection Temperature at 1.8 MPa (264 psi) 46.7 - 87.2 °C
116 - 189 °F
Average value: 70.7 °C Grade Count:43
Vicat Softening Point 63.0 - 91.0 °C
145 - 196 °F
Average value: 76.4 °C Grade Count:30
Softening Point 160 - 190 °C
320 - 374 °F
Average value: 174 °C Grade Count:7
Minimum Service Temperature, Air -57.5 - -22.3 °C
-71.5 - -8.14 °F
Average value: -41.9 °C Grade Count:8
Brittleness Temperature -72.0 - -3.00 °C
-97.6 - 26.6 °F
Average value: -36.8 °C Grade Count:179
Decomposition Temperature 185 - 200 °C
365 - 392 °F
Average value: 188 °C Grade Count:5
UL RTI, Electrical 50.0 - 80.0 °C
122 - 176 °F
Average value: 56.0 °C Grade Count:5
UL RTI, Mechanical with Impact 50.0 - 70.0 °C
122 - 158 °F
Average value: 54.0 °C Grade Count:5
UL RTI, Mechanical without Impact 50.0 - 80.0 °C
122 - 176 °F
Average value: 56.0 °C Grade Count:5
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:51
Oxygen Index 25.0 - 31.0 %
25.0 - 31.0 %
Average value: 28.6 % Grade Count:14
Optical Properties Metric English Comments
Haze 5.00 - 16.0 %
5.00 - 16.0 %
Average value: 8.00 % Grade Count:8
Transmission, Visible 66.0 - 90.0 %
66.0 - 90.0 %
Average value: 84.9 % Grade Count:47
Component Elements Properties Metric English Comments
Cadmium, Cd 0.00500 %
0.00500 %
Average value: 0.00500 % Grade Count:9
Chromium, Cr 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:9
Lead, Pb 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:9
Mercury, Hg 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:9
Electrical Properties Metric English Comments
Electrical Resistivity 2.00e+6 - 1.00e+15 ohm-cm
2.00e+6 - 1.00e+15 ohm-cm
Average value: 1.52e+14 ohm-cm Grade Count:18
>= 2.00e+10 ohm-cm

@Temperature 70.0 - 70.0 °C
>= 2.00e+10 ohm-cm

@Temperature 158 - 158 °F
Average value: 1.05e+12 ohm-cm Grade Count:5
Surface Resistance 1.00e+12 - 5.00e+14 ohm
1.00e+12 - 5.00e+14 ohm
Average value: 2.00e+14 ohm Grade Count:3
Dielectric Strength 6.00 - 35.0 kV/mm
152 - 889 kV/in
Average value: 20.3 kV/mm Grade Count:3
Comparative Tracking Index 400 - 600 V
400 - 600 V
Average value: 575 V Grade Count:4
Processing Properties Metric English Comments
Melt Temperature 154 - 213 °C
310 - 415 °F
Average value: 179 °C Grade Count:121
Drying Temperature 54.4 - 68.3 °C
130 - 155 °F
Average value: 59.1 °C Grade Count:3