Isoflon PTFE Polytetrafluoroethylene
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Molded |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon PTFE Polytetrafluoroethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Fluoropolymer material specifications.Information provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.13 - 2.18 g/cc | 2.13 - 2.18 g/cc | ISO 12086 |
| Water Absorption | 0.0010 % | 0.0010 % | DIN 53 495 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 54 - 60 | 54 - 60 | DIN 53 505 |
| Ball Indentation Hardness | 23.0 - 28.0 MPa | 3340 - 4060 psi | DIN 53 456 |
| Tensile Strength | 20.0 - 30.0 MPa | 2900 - 4350 psi | DIN 53455 |
| Elongation at Break | 200 - 300 % | 200 - 300 % | DIN 53455 |
| Tensile Modulus | 0.600 - 0.700 GPa | 87.0 - 102 ksi | DIN 53457 |
| Coefficient of Friction, Dynamic | 0.070 | 0.070 | on steel |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C @Temperature 20.0 - 100 °C |
66.7 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous |
| Minimum Service Temperature, Air | -200 °C | -328 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 20.0 - 70.0 kV/mm | 508 - 1780 kV/in | DIN 53481 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 35 FRC 5 PA6 reinforced with 35% glass fibre, with flame retardant
- Chevron Phillips 7109BKT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F)
- Saint-Gobain Norcrylâ„¢ A1000 Solid Acrylic Bonding Tape
- Sylvin Technologies 5108 PVC Wire/Cable Compound
- Borealis Visico™ LE4481/LE4437 Moisture-Crosslinking Polyethylene Compound for Flexible Low Voltage Insulation
- Vyncolit G885 Novolac Phenolic
- Zeon Chemicals Nipol® 33-5SR Nitrile Elastomer
- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- ChevronTexaco Aries® 100
Copyright © lookpolymers.com All Rights Reserved