Carmel Olefins IPETHENE® 4203 Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade
Manufacturer Carmel Olefins
Trade Name IPETHENE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carmel Olefins IPETHENE® 4203 Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
IPETHENE® 4203 is a low density polyethylene extrusion grade. It exhibits good impact and puncture resistance, very good bubble stability in thick-gauge blown film processing, and excellent ESCR. APPLICATIONS IPETHENE® 4203 is used for production of irrigation pipe systems, 80 to 250 µm films for heavy duty and shrink packaging, greenhouses, net coverings, and industrial applications.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ISO 1183-A
ESCR 10% Igepal® 20 hour
20 hour
F50; ASTM D1693
Thickness 100 microns
3.94 mil
Melt Flow 0.20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 330 %
330 %
ISO 1184
Film Elongation at Break, TD 480 %
480 %
ISO 1184
Elmendorf Tear Strength MD 250 g
250 g
ISO 6283-2
Elmendorf Tear Strength TD 500 g
500 g
ISO 6283-2
Elmendorf Tear Strength, MD 2.50 g/micron
63.5 g/mil
ISO 6283-2
Elmendorf Tear Strength, TD 5.00 g/micron
127 g/mil
ISO 6283-2
Dart Drop 6.50 g/micron
165 g/mil
F50; ISO 7765-A
Dart Drop Test 650 g
1.43 lb
F50; ISO 7765-A
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ISO 1184
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ISO 1184
Processing Properties Metric English Comments
Melt Temperature 220 °C
428 °F
Blow-up Ratio (BUR) 2.0
2.0