- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyphenylene Ether/PPO
- Polyphenylene Ether, 20% Glass Filled
- Beijing Chemical Industry KAIFA® M109-G20N MPPO Resin
Beijing Chemical Industry KAIFA® M109-G20N MPPO Resin
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® M109-G20N MPPO Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 3.20 mm |
V-1 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 1e+6 Hz |
0.0030 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 275 °C | 527 °F | |
| Middle Barrel Temperature | 290 °C | 554 °F | |
| Front Barrel Temperature | 290 °C | 554 °F | |
| Nozzle Temperature | 290 °C | 554 °F | |
| Mold Temperature | 100 °C | 212 °F | |
| Injection Pressure | 140 MPa | 20300 psi | |
| Cycle Time - Injection | 25 - 30 sec | 25 - 30 sec | |
| Screw Speed | 60 rpm | 60 rpm |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRESEAL 6070 Ag-Coated Glass
- LyondellBasell Petrothene® NA206000 Low Density Polyethylene
- Lord Adhesives Metech 7806A Cermet Resistor Overglaze Composition
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Lubrizol ESTANE® GP85AB Ester Based Thermoplastic Polyurethane
- Eagle Brass 706 Copper Nickel 10%, 1/2 Hard
- Dow Corning SYL-OFF® SL 800 COATING
- Azoty Tarnow™ Tarnamid® T-29 MCS Polyamide 6 - Colored
- Bhansali Engineering Abstron IM-11 ABS Injection Molding Grade
- Arkema Group Kynar® FLEX 2801 PVDF (discontinued **)
Copyright © lookpolymers.com All Rights Reserved