SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Aramid Fiber Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KAL22 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Fiber. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | on Tensile Bar; SABIC Method |
| >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 7.4 % | 7.4 % | Type I, 5 mm/min; ASTM D638 |
| 7.4 % | 7.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.3 % | 6.3 % | 5 mm/min; ISO 527 |
| 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.45 GPa | 500 ksi | 1 mm/min; ISO 527 |
| 3.63 GPa | 526 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 77.0 MPa | 11200 psi | ISO 178 |
| Flexural Modulus | 3.07 GPa | 445 ksi | 2 mm/min; ISO 178 |
| 3.09 GPa | 448 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.12 J/cm | 9.59 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D3702 Modified |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 2752 Liquid Silicone Rubber - Self-Bonding
- LATI Latistat 83-05 POM, Impact Modified
- Süd-Chemie Nanofil® 9 Polymer Additive
- Sichuan Deyang Haton® hMR60DL Polyphenylene Sulfide, Glass & Mineral Reinforced
- Polyram PlusTek PA340S8 Nylon 6.6 for Injection Molding, 40% Glass-beads Reinforced
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Atomite Whiting Filler
- Eastman Tenite Butyrate 530E3720010 Clear, Trsp Cellulose Acetate Butyrate
- Daikin NEOFLON EP-620 ETFE Pellets
- Carmel Olefins IPETHENE® 213 Low Density Polyethylene
- DSM Arnite® TV4 460 KL PBT/PET Blend-30% Glass Reinforced (European Grade)
Copyright © lookpolymers.com All Rights Reserved