Inno-Comp INNOPOLÂ® CS 2-4210 10% Chalk-Filled Polypropylene Block-Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Calcium Carbonate (CaCO3) Filler
Manufacturer	Inno-Comp Ltd
Trade Name	INNOPOL® CS
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Inno-Comp INNOPOLÂ® CS 2-4210 10% Chalk-Filled Polypropylene Block-Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

INNOPOLÂ® CS 2-4210 is a 10% chalk-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-4210 is developed for producing injection molded components.All information provided by INNO-COMP.

Physical Properties	Metric	English	Comments
Density	0.970 g/cc @Temperature 23.0 Â°C	0.0350 lb/inÂ³ @Temperature 73.4 Â°F	ISO 1183
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	7.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.0 MPa	3480 psi	50 mm/min; ISO 527-1,-2
Elongation at Yield	4.5 %	4.5 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	1.35 GPa	196 ksi	1 mm/min; ISO 527-1,-2
Flexural Modulus	1.50 GPa	218 ksi	2 mm/min; ISO 178
Charpy Impact, Notched	0.400 J/cmÂ² @Temperature -20.0 Â°C	1.90 ft-lb/inÂ² @Temperature -4.00 Â°F	ISO 179/1eA
	0.900 J/cmÂ² @Temperature 23.0 Â°C	4.28 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	100 Â°C	212 Â°F	ISO 75-1,-2

Descriptive Properties	Value	Comments
Color	Natural