Inno-Comp INNOPOLÂ® CS 2-3120 20% Talc Filled Polypropylene Block-Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer	Inno-Comp Ltd
Trade Name	INNOPOL® CS
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Inno-Comp INNOPOLÂ® CS 2-3120 20% Talc Filled Polypropylene Block-Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

INNOPOLÂ® CS 2-3120 is a 20% talc filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-3120 is developed for producing injection molded components.All information provided by INNO-COMP.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc @Temperature 23.0 Â°C	0.0376 lb/inÂ³ @Temperature 73.4 Â°F	ISO 1183
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 230 Â°C	12 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min; ISO 527-1,-2
Elongation at Yield	3.5 %	3.5 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	2.50 GPa	363 ksi	1 mm/min; ISO 527-1,-2
Flexural Modulus	2.60 GPa	377 ksi	2 mm/min; ISO 178
Charpy Impact, Notched	0.140 J/cmÂ² @Temperature -30.0 Â°C	0.666 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	0.380 J/cmÂ² @Temperature 23.0 Â°C	1.81 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	123 Â°C	253 Â°F	ISO 75-1,-2

Descriptive Properties	Value	Comments
Color	Natural