Ineos Styrenics 496N High-Impact Polystyrene Resin (NAFTA)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics 496N High-Impact Polystyrene Resin (NAFTA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High-impact, lower flow grades for food packaging, dairy containers, lids, plates, appliance components and housings.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 58 | 58 | ASTM D785 |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
| Tensile Strength, Yield | 23.5 MPa | 3410 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Tensile Modulus | 2.137 GPa | 310.0 ksi | ASTM D638 |
| Flexural Modulus | 1.689 GPa | 245.0 ksi | ASTM D790-1 |
| Izod Impact, Notched | 1.49 J/cm | 2.80 ft-lb/in | ASTM D256-A |
| Gardner Impact | 36.2 J @Thickness 3.17 mm, Temperature 23.0 °C |
26.7 ft-lb @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D5420, GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
all colors |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 60 % | 60 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion |
| 180 - 280 °C | 356 - 536 °F | Molding |
Users viewing this material also viewed the following:
- Polymax® Maxelast® D6890 TPE, Extruded
- Pacific Sintered Materials FX-232-T(HT) Infiltrated High Carbon Steel Powdered Metal
- Glastic SG-200 Corner Angles
- Sylvin Technologies 8999-90 Natural PVC Extrusion Compound
- SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copoly (Asia Pacific)
- EMS-Grivory Grivory® TSM-30/2 PA666-MD30
- Engineered Plastics EPPC 2014G Polycarbonate
- 3M FM123 Indoor UL Recognized White Polyester Label Products
- BASF Ultramid® 8232G HS FR 25% Glass Fiber Fire Retardant PA6 (Dry)
- BASF Styropor® BF 222 EPS
Copyright © lookpolymers.com All Rights Reserved