Nylene® PA6 Impact Modified 323 HS Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Nylene® |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nylene® PA6 Impact Modified 323 HS Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion Grade; Dry as molded.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D955 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 315 % | 315 % | ASTM D638 |
| Flexural Modulus | 0.520 GPa | 75.4 ksi | ASTM D790 |
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 °C | 410 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Total Finathene® 7208 HDPE extrusion resin (discontinued **)
- SABIC Innovative Plastics NORYL PX1543 PPE+PS (Asia Pacific)
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=6.5, Diameter 0.4 mm)
- Daikin NEOFLON AP-201SH PFA Semiconductor Grade
- Chicago Extruded Metals BioBrass® UNS C63000 Aluminum Bronze
- Fainplast Compounds GS 70/BT Flexible PVC, Injection Molding for Footwear
- Azoty Tarnow™ Tarnamid® T-27 GF15 FRV0 Polyamide 6 - Flame Retarded, Reinforced
- Zhejiang Juner PC-A1-9A Top-Grade Flame Retardant UV-Resistant
- Axiall 46234A Moldings & Extrusions Flexible PVC
- Arkema Group Oroglas® V 045 I Acrylic, Extrusion Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved