- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend
- Ineos ABS Triax® KU2-3154 ABS + Nylon 6
Ineos ABS Triax® KU2-3154 ABS + Nylon 6
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon , Nylon 6 |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® KU2-3154 ABS + Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral reinforced, easy flowing, reduced moisture absorption, very low warpage, injection molding, pellets.,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | dry |
| Water Absorption | 3.9 % | 3.9 % | dry |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | dry |
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | conditioned |
| 55.0 MPa | 7980 psi | dry | |
| Elongation at Break | 35 % | 35 % | Nominal, dry |
| Elongation at Yield | 2.9 % | 2.9 % | dry |
| 4.0 % | 4.0 % | conditioned | |
| Tensile Modulus | 2.00 GPa | 290 ksi | conditioned |
| 2.70 GPa | 392 ksi | dry | |
| Charpy Impact Unnotched | 15.0 J/cm² | 71.4 ft-lb/in² | dry |
| 15.0 J/cm² | 71.4 ft-lb/in² | conditioned | |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
conditioned | |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
dry | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | conditioned |
| 0.800 J/cm² | 3.81 ft-lb/in² | dry |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.650 µm/m-°C @Temperature 20.0 °C |
0.361 µin/in-°F @Temperature 68.0 °F |
dry, parallel |
| CTE, linear, Transverse to Flow | 1.00 µm/m-°C @Temperature 20.0 °C |
0.556 µin/in-°F @Temperature 68.0 °F |
dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | dry |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | dry |
| Vicat Softening Point | 105 °C | 221 °F | dry |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
dry |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | conditioned |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
Dry |
| 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
conditioned | |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
Dry | |
| 5.0 @Frequency 100 Hz |
5.0 @Frequency 100 Hz |
conditioned | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | dry |
| 40.0 kV/mm | 1020 kV/in | conditioned | |
| Dissipation Factor | 0.015 @Frequency 100 Hz |
0.015 @Frequency 100 Hz |
dry |
| 0.015 @Frequency 1e+6 Hz |
0.015 @Frequency 1e+6 Hz |
dry | |
| 0.040 @Frequency 1e+6 Hz |
0.040 @Frequency 1e+6 Hz |
conditioned | |
| 0.065 @Frequency 100 Hz |
0.065 @Frequency 100 Hz |
conditioned | |
| Comparative Tracking Index | 600 V | 600 V | dry |
Users viewing this material also viewed the following:
- Nylene® 453 Nylon 6, 50% RH
- Victrex® PEEK 90GL60 Polyetheretherketone, 60% Glass Fibre Reinforced
- Chevron Phillips Marlex® CL-200YB (Black) Rotational molding crosslinkable high density polyethylene (discont
- Isoflon PTFE + 60% Bronze Polytetrafluoroethylene with 60% Bronze
- Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet
- ExxonMobil Spartan EP 680
- Bapolene® 152B Polyethylene Film Grade
- ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 482°C (UNS S41600)
- 3M 9471PC Adhesive Transfer Tapes with Adhesive 300
- Multibase Multibatch® MP 52518 BOPP White Pearlised Film
Copyright © lookpolymers.com All Rights Reserved