Ineos ABS Lustran® QE 1088 FC, Injection Grade (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS Lustran® QE 1088 FC, Injection Grade (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Injection molding grade, high impact, medium gloss.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³
Melt Flow	17 g/10 min @Load 10.0 kg, Temperature 220 °C	17 g/10 min @Load 22.0 lb, Temperature 428 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	48.0 MPa	6960 psi
Elongation at Yield	2.0 %	2.0 %
Tensile Modulus	2.60 GPa	377 ksi
Charpy Impact Unnotched	0.800 J/cm² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	2.00 J/cm²	9.52 ft-lb/in²

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature 20.0 °C	44.4 µin/in-°F @Temperature 68.0 °F
Vicat Softening Point	98.0 °C	208 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	3.2 @Frequency 1e+6 Hz	3.2 @Frequency 1e+6 Hz
	3.5 @Frequency 100 Hz	3.5 @Frequency 100 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.014 @Frequency 100 Hz	0.014 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V