- Acrylonitrile Butadiene Styrene (ABS), Molded
- Ineos ABS Lustran® LGA
Ineos ABS Lustran® LGA
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® LGA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:UnfilledSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 22 g/10 min @Load 10.0 kg, Temperature 220 °C |
22 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.5 MPa | 5290 psi | |
| Elongation at Break | 14 % | 14 % | Nominal |
| Elongation at Yield | 3.3 % | 3.3 % | |
| Tensile Modulus | 2.20 GPa | 319 ksi | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Vicat Softening Point | 96.0 °C | 205 °F | 50°C/h 50N |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL Recognized |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL Recognized |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |
| Injection Pressure | 55.0 MPa | 7980 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 945A PC (Asia Pacific)
- Overview of materials for Acetal Homopolymer, Unreinforced
- Freudenberg Simrit V176 Standard Fluoroelastomer
- LG Chemical LUPOY HI-1002 High Impact Modified PC, Unreinforced
- Multibase Multi-Flex® A 3540 TPE Thermoplastic Elastomer
- Techmer ES HiFill® PP GB30 30% Glass Beads Filled
- Samsung Cheil Industries Infino® CF-1050 PC, Unreinforced High Impact
- SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Asia Pacific)
- A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6
Copyright © lookpolymers.com All Rights Reserved