Ineos ABS Lustran® H607AS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® H607AS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Contains antistatic additives,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| Tensile Modulus | 2.40 GPa | 348 ksi | |
| Charpy Impact Unnotched | 13.0 J/cm² | 61.9 ft-lb/in² | |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.800 µm/m-°C @Temperature 20.0 °C |
0.444 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | |
| Vicat Softening Point | 100 °C | 212 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
|
| 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Chevron Phillips HiD® 9638 HDPE Sheeting and Blown Film Resin (discontinued **)
- KYDEX® 5555 MB Low Heat Release Aviation Thermoforming Sheet with Microban® Antimicrobial
- Tipco Tipcolite® TMS 111 Phenolic Compound, Cellulose Pulp, in fluffy form, having Soft Flow & High Strength
- Cheng Yu Plastic N6CV1 Flame Retardant Nylon 6, 10% Mineral Reinforced
- EMS-Grivory Grivory® AS/2 PA66
- Dow CYRACURE™ UVR-6128 Cycloaliphatic Epoxide
- ACC MM906 Condensation Cure 2-Part Molding Rubber
- DSM Akulon® F132-E Nylon 6 (European Grade) (Dry) (discontinued **)
- Sinotek Materials MD-3 Graphite Emulsion
Copyright © lookpolymers.com All Rights Reserved