LG Chemical SEETEC R3420 Polypropylene, Random Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC R3420 Polypropylene, Random Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Seetec R3420 is a polypropylene-ethylene random copolymer designed for the production of cast films. It has a good clarity due to the optimum content of ethylene and offers optimum balance between optical properties and physical strength. It is suitable for the general purpose of coextruded cast film in food packaging or semi retort pouch being required non slip and medium heat seal temperature. SEETEC R3420 meets the FDA requirement in the code of Federal Regulations in 21 CFR 177.1520 for food contact. Applications: CPP Film (Non Slip)CAS No. 9010-79-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D1505 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ASTM D785 |
| Tensile Strength, Yield | 26.5 MPa | 3840 psi | 50mm/min; ASTM D638 |
| Film Elongation at Break, MD | >= 500 % | >= 500 % | ASTM D882 |
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ASTM D882 |
| Elongation at Break | <= 500 % | <= 500 % | 50mm/min; ASTM D638 |
| Flexural Modulus | 0.883 GPa | 128 ksi | ASTM D760 |
| Izod Impact, Notched | 0.490 J/cm @Temperature 23.0 °C |
0.918 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Film Tensile Strength at Break, MD | 440 MPa | 63800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 340 MPa | 49300 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 130 - 170 °C | 266 - 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Vicat Softening Point | 134 °C @Load 1.00 kg |
273 °F @Load 2.20 lb |
ASTM D1525 |
| Flash Point | >= 340 °C | >= 644 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.3 % | 1.3 % | ASTM D1003 |
| Gloss | 135 % | 135 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Temperature | 130°C | >1 Kgf, LG Method |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V75C Fluoroelastomer Compound
- PolyOne Edgetek® PI-30GF/000 Polyether Imide (PEI)
- Silberline SilBerCote® PC 0452Z
- Silberline Stamford "A3"
- Hexcel® Redux® 112 Surface Pretreatment Protection Solution
- ELASTO UK Dryflex® 400601S SBS Based Material, 60A Hardness, Natural
- 3M Scotch® 824 Pouch Tape
- Resinlab® EP1026 Clear Epoxy Adhesive
- Braskem RP 145 RACO Random Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved