Ineos ABS Lustran® ABS 595CP Refrigeration and Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 595CP Refrigeration and Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 595CP is refrigeration and extrusion grade, resistant to cyclopentane, and has high impact strength.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ISO 2039-2 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 25 % | >= 25 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 2.55 GPa | 370 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 15.0 kJ/m² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
ISO 180-1A | |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75-1,-2 |
| Vicat Softening Point | 102 °C @Load 5.10 kg |
216 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 90 % | 90 % | Angle 60°; ISO 2813 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Asia Pacific)
- Fiberfil® J-68/30/E Polypropylene Copolymer, 30% Glass Fiber Reinforced, Chemically coupled
- Karina E 800-10/1-AY-RT PVC Compound White Color
- Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 6 PHR Di-Cup 40C
- ConocoPhillips Syncon® 22 Synthetic AW Hydraulic Fluid 22
- Cossa Polimeri ESTADIENE 1030 V0/F Flame Retardant ABS
- Dow Corning XIAMETER® PMCPMEM-0346 Emulsion
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Thanecure® ZM
Copyright © lookpolymers.com All Rights Reserved