Huntsman IROGRAN® A 95 H 4678 Polyester-Based TPU-Injection Molding Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 95 H 4678 Polyester-Based TPU-Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 92 H 4656 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are short cycle times, good melt flow and easy demolding. Performance Features: Good melt flow Easy demolding Short cycle times Easy coloring recyclable Applications: For the production of technical parts, wheels and rollers, cover plates, coupling halves, conveyor rollers.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D995 |
| Melt Index of Compound | 90 g/10 min @Load 10.0 kg, Temperature 210 °C |
90 g/10 min @Load 22.0 lb, Temperature 410 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | DIN 53504 |
| Elongation at Break | 690 % | 690 % | ASTM D412 |
| 100% Modulus | 0.0111 GPa | 1.61 ksi | DIN 53504 |
| 300% Modulus | 0.0198 GPa | 2.87 ksi | DIN 53504 |
| Rebound | 30 % | 30 % | Bayshore; ASTM D2632 |
| Tear Strength | 151 kN/m | 860 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 24 % @Temperature 23.0 °C, Time 252000 sec |
24 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 43 % @Temperature 70.0 °C, Time 86400 sec |
43 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 180 - 190 °C | 356 - 374 °F | Huntsman/TMA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
Users viewing this material also viewed the following:
- Osprey Metals 316L/MA Master Alloy Stainless Steel Powder (Grade 95% - 16)
- SABIC Innovative Plastics Geloy XP4034 ASA (Europe-Africa-Middle East)
- Lanxess Durethan® AKV 30 H3.0 000000 Nylon 66, 30% Glass Fibers
- Samsung Cheil Industries Infino® HI-1001B PC/ABS, Unreinforced
- Borealis Borcell™ HE1102 High Density Polyethylene Compound for Gas Injection of Cellular Communication Cable Insulation
- Arkema Group LOTRYL® Bestpeel 2407 Copolymer Ethylene - Methyl Acrylate
- BASF Ultradur® B 4560 PBT
- Axiall 7020 Rigid PVC, Extrusion
- TIMCAL TIMREX® KS300-1250 Primary Synthetic Graphite
Copyright © lookpolymers.com All Rights Reserved