Huntsman IROGRAN® A 92 P 4851 Ether-Based TPU-For Cable Industry
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 P 4851 Ether-Based TPU-For Cable Industry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 92 P 4851 is a thermoplastic polyether- polyurethane for injection molding and extrusion applications. Additional characteristics of the product are high extrudability and low-adhesion surfaces. Performance Features: Excellent hydrolysis resistance High microbial resistance High stability of melt High production rates Low-adhesion surfacesApplications: For the production of jacket material for cables, jackets for high pressure hose spiral hoses, profilesInformation provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | |
| Melt Index of Compound | 55 g/10 min @Load 21.6 kg, Temperature 190 °C |
55 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 |
| Elongation at Break | 500 % | 500 % | DIN 53504 |
| 100% Modulus | 0.0100 GPa | 1.45 ksi | DIN 53504 |
| 300% Modulus | 0.0160 GPa | 2.32 ksi | DIN 53504 |
| Rebound | 33 % | 33 % | Bayshore |
| Tear Strength | 65.0 kN/m | 371 pli | ISO 34-1 |
| Abrasion | 35 | 35 | mm<sup>3</sup>; ISO 4549 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 86400 sec |
25 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D395 |
| 45 % @Temperature 70.0 °C, Time 86400 sec |
45 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 - 171 °C | 320 - 340 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- PolyOne Versalloy™ XL 9045-1 Thermoplastic Elastomer (TPE)
- PolyOne Bergamid™ A700 G20 UF Polyamide 66 (Nylon 66)
- Overview of materials for Nylon 11 with 30% Glass Fiber Filler
- Shandong Dongyue Shenzhou New Material Co DS606 Fluorinated Ethylene Propylene Powder
- Supreme Petrochem SC 203 LV General Purpose Polystyrene
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- Chesterton MRS S4+ Metal Rebuilding System
- CEN® Electronic Material CTS Polyimide Resin
- DuPont Teijin Films Mylar® MDA Polyester Film, 200 Gauge
- Axiall 34311 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved