Azdel Plus C401B02N 40% Chopped Fiber Mat / PP Resin Matrix

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Azdel
Trade Name Plus
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azdel Plus C401B02N 40% Chopped Fiber Mat / PP Resin Matrix.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AZDEL® C401B02N is a chopped fiber material based on random oriented long chopped glass fiber mat (paper making process). This polypropylene composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural, thin wall applications.Commercially available only to European based customers.Information provided by Azdel.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
Laminate; ISO 2577
1.22 g/cc
1.22 g/cc
Molded plaque; ISO 2577
Filler Content 40 %
40 %
AZDEL Test
Thickness 3900 microns
154 mil
AZDEL Test
Linear Mold Shrinkage 0.0025 cm/cm
0.0025 in/in
320 x 320 mm flat plaque; ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527/4
Elongation at Break 2.5 %
2.5 %
ISO 527/4
Tensile Modulus 5.50 GPa
798 ksi
ISO 527/4
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 5.60 GPa
812 ksi
ISO 178
Charpy Impact, Notched 8.50 J/cm²
40.5 ft-lb/in²
ISO 179/2fn
Impact 5500

@Thickness 4.00 mm
5500

@Thickness 0.157 in
Multi-axial in Newtons, at max. force; ISO 6603-2
Impact Test 17.0 J

@Thickness 4.00 mm
12.5 ft-lb

@Thickness 0.157 in
Multi-axial, at max. force; ISO 6603-2
45.0 J

@Thickness 4.00 mm
33.2 ft-lb

@Thickness 0.157 in
Multi-axial, total energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 29.0 µm/m-°C

@Temperature 0.000 - 120 °C
16.1 µin/in-°F

@Temperature 32.0 - 248 °F
100 x 15 x 3 mm sample; AZDEL Test
44.0 µm/m-°C

@Temperature -30.0 - 0.000 °C
24.4 µin/in-°F

@Temperature -22.0 - 32.0 °F
100 x 15 x 3 mm sample; AZDEL Test
Melting Point 115 °C
239 °F
Recrystallizing temperature; ISO 3146
155 °C
311 °F
ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
ISO 75/2a
Processing Properties Metric English Comments
Processing Temperature 205 - 220 °C
401 - 428 °F
Surface temperature
Mold Temperature 30.0 - 90.0 °C
86.0 - 194 °F
Back Pressure 15.0 - 25.0 MPa
2180 - 3630 psi
Depending on wall thickness and part complexity