- Huntsman IROGRAN® A 92 H 4656 Polyester-Based TPU-Injection Molding Grade
Huntsman IROGRAN® A 92 H 4656 Polyester-Based TPU-Injection Molding Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 H 4656 Polyester-Based TPU-Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 92 H 4656 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are short cycle times, good melt flow and easy demolding. Performance Features: Good melt flow Easy demolding Short cycle times Easy coloring recyclableApplications: For the production of technical parts, wheels and rollers, cover plates, coupling halves, conveyor rollersInformation provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D995 |
| Melt Index of Compound | 90 g/10 min @Load 10.0 kg, Temperature 210 °C |
90 g/10 min @Load 22.0 lb, Temperature 410 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Hardness, Shore D | 40 | 40 | ASTM D2240 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | DIN 53504 |
| Elongation at Break | 740 % | 740 % | ASTM D412 |
| 100% Modulus | 0.00890 GPa | 1.29 ksi | DIN 53504 |
| 300% Modulus | 0.0186 GPa | 2.70 ksi | DIN 53504 |
| Rebound | 32 % | 32 % | Bayshore; ASTM D2632 |
| Tear Strength | 135 kN/m | 770 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec |
25 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 43 % @Temperature 70.0 °C, Time 86400 sec |
43 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 - 185 °C | 338 - 365 °F | Huntsman/TMA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 5118N (18601) Linear Low Density Polyethylene
- Phillips 66 COPYLENE® CH120LN Polypropylene, Homopolymer, Injection Molding, Antistat/Lube
- Taiwan PU Corporation TPUA-1560 TPU Shoe Adhesive
- SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
- Silberline Sparkle Silver® 7000-AR
- Chesterton ARC 982 100% Novolac acid resistant coating
- Arkema Group Pebax® 3533 SA 01 MED Polyether Block Amide (PEBA)
- 3A Composites Core Materials AIREX® PXw.420 Fiber-Reinforced Structural Foam Panel
Copyright © lookpolymers.com All Rights Reserved