- Honeywell Capran® Oxyshield™ OMBS (1.00 mil) Monoaxially Oriented, Co-Extruded Nylon 6-Based Clear Film
Honeywell Capran® Oxyshield™ OMBS (1.00 mil) Monoaxially Oriented, Co-Extruded Nylon 6-Based Clear Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Oxyshield™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Oxyshield™ OMBS (1.00 mil) Monoaxially Oriented, Co-Extruded Nylon 6-Based Clear Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Oxyshieldâ„¢ Oriented Medium Barrier is a 1.00 mil (25 micron) monoaxially oriented, coextruded nylon 6/EVOH/nylon 6 clear film with slip additive having excellent gas barrier through moderate relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in³ | Yield Density |
| Oxygen Transmission Rate | 1.55 cc/m²/day | 0.0998 cc/100 in²/day | 73°F (23°C) / 65%RH; ASTM D3985 |
| Thickness | 25.4 microns | 1.00 mil | |
| Surface Tension | >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 66.2 - 75.8 MPa | 9600 - 11000 psi | ASTM D882 |
| Film Elongation at Break, MD | 60 - 85 % | 60 - 85 % | ASTM D882 |
| Film Elongation at Break, TD | 260 - 440 % | 260 - 440 % | ASTM D882 |
| Secant Modulus, MD | 2.586 - 3.516 GPa | 375.1 - 510.0 ksi | ASTM D882 |
| Secant Modulus, TD | 2.413 - 2.896 GPa | 350.0 - 420.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | film to stainless steel; ASTM D1894 |
| 0.70 - 0.80 | 0.70 - 0.80 | film to film; ASTM D1894 | |
| Tear Strength Test | 1000 - 1600 | 1000 - 1600 | graves tear TD, grams/mil; ASTM D1004 |
| 1100 - 1650 | 1100 - 1650 | graves tear MD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 269 - 379 MPa | 39000 - 55000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 62.1 - 103 MPa | 9000 - 15000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | <= 8.0 % | <= 8.0 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= 1.5 % | <= 1.5 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 6.0 % | <= 6.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8182R (837RP) (UF) Synthetic Oil
- Nylacast POM C Acetal Copolymer
- PolyOne Dynaflex™ G2730 Thermoplastic Elastomer (TPE)
- Polimersan Plastics POLIPA® (PA 6) Polyamide
- Flint Hills AP6835-HS Polypropylene Impact Copolymer
- Kraton® D1161 B (SIS) Linear Block Copolymer
- LG Chemical HF-350 ABS, High Flow, High Impact
- Lucobit Lucofin® 1455MB Polyolefin TPO Granules, Black
- DuPont Performance Polymers Zytel® HTN 54G15HSLR NC010 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved