SABIC Innovative Plastics Valox® CS815 PBT+PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® CS815 PBT+PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% glass reinforced PBT+PET. Improved heat aged color stability, high surface gloss. Oven knobs and handles, kickplates, trim.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.50 J/cm | 4.68 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C @Thickness 3.20 mm |
356 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8021 BLK , 37.5% Filler Content
- MV Labs TL100 TlC2H3O2 Thallium(I) acetate
- Victrex® PEEK 150GL15 Polyetheretherketone, 15% Glass Fibre Reinforced
- H.C. Starck 2602 Molybdenum Powder Metallurgy Alloy ODS Mo-La
- SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66
- Samyang Tribit® 1500GN15 Polybutylene Terephthalate, 15% Glass Reinforced, Flame Retardant
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- Eagle Brass 110 EPT COPPER, 1/4 Hard
- Sumitomo Bakelite North America RX® 1-510N Mineral Filled Diallyl Phthalate
- Materion Beryllium Copper Alloy 3 Tube; A (TB00) Temper; All Sizes (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved