SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High modulus/impact/heat PPE+PP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 260 °C |
14 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 125 % | 125 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.24 GPa | 180 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 51.0 MPa | 7400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.37 GPa | 199 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 44.0 J @Temperature -30.0 °C |
32.5 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 162 µm/m-°C @Temperature -40.0 - 40.0 °C |
90.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 97.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 86.0 °C | 187 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Permabond TA4202 Toughened Acrylic Adhesive
- SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Europe-Africa-Middle East)
- Albis Plastics Tedur® L 9521-1 PPS, 60% Glass Fiber/Mineral (discontinued **)
- Menzolit Menzolit® SMC 0160 Unsaturated Polyester UP
- Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.50 inch (12.7 mm) o.d. and 0.050 inch (1.27 mm) Thickness
- E-Polymers TEKAFIN® PH40FR Flame Retardant Heat Resistance Compounded-PP
- Carpenter Vega® Alloy Tool Steel (Air-Tough) (AISI A6)
- 3M S38 Glass Bubbles
- Toyobo Diaflora® DS 2220B
Copyright © lookpolymers.com All Rights Reserved