- HOME
- POLYMER SEARCH
- Film
- Honeywell Aegisâ„¢ H155MP Nylon 6 Extrusion Grade Homopolymer Film
Honeywell Aegisâ„¢ H155MP Nylon 6 Extrusion Grade Homopolymer Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Honeywell |
| Trade Name | Aegis™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Aegisâ„¢ H155MP Nylon 6 Extrusion Grade Homopolymer Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Aegis H155MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermo-forming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.Applications:Processed MeatFresh Red MeatPoultryFishCheeseDried FoodChilled Fruit JuicesInformation provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Permeability | 992 g mil/ (m2 day) @Temperature 38.0 °C |
64.0 g mil/ (100 in2 day) @Temperature 100 °F |
ASTM F1249 |
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D1505 |
| Water Absorption | 0.70 % | 0.70 % | Extractable Content |
| 1.6 % | 1.6 % | in 24 hours | |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | at 50% RH |
| Water Absorption at Saturation | 9.5 % | 9.5 % | |
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | |
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Viscosity Measurement | 4.0 | 4.0 | 96% Sulfuric Acid |
| 155 | 155 | FAV; ASTM D789 | |
| Maximum Moisture Content | 0.080 | 0.080 | |
| Melt Flow | 1.1 g/10 min @Load 1.00 kg, Temperature 235 °C |
1.1 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Molded; ASTM D882 |
| Film Tensile Strength at Yield, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 |
| Film Elongation at Break, TD | 290 % | 290 % | ASTM D882 |
| Elongation at Break | 3.8 % | 3.8 % | Molded; ASTM D882 |
| Tensile Modulus | 0.570 GPa | 82.7 ksi | TD; ASTM D882 |
| 0.630 GPa | 91.4 ksi | MD; ASTM D882 | |
| 3.02 GPa | 438 ksi | Molded; ASTM D882 | |
| Flexural Strength | 100 MPa | 14500 psi | Molded; ASTM D790 |
| Flexural Modulus | 2.61 GPa | 379 ksi | Molded; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | Molded; ASTM D256 |
| Tear Strength, Total | 2510 N | 564 lb (f) | Graves, MD; ASTM D1004 |
| 2590 N | 582 lb (f) | Graves, TD; ASTM D1004 | |
| Elmendorf Tear Strength MD | 74400 g | 74400 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 93800 g | 93800 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 90.0 MPa | 13100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 70.0 MPa | 10200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Cast Film |
| 246 - 254 °C | 475 - 489 °F | Tubular (Blown) Film | |
| Adapter Temperature | 260 °C | 500 °F | Tubular (Blown) Film |
| 260 - 266 °C | 500 - 511 °F | Cast Film | |
| Die Temperature | 254 °C | 490 °F | Tubular (Blown) Film |
| 260 °C | 500 °F | Cast Film | |
| Melt Temperature | 254 - 260 °C | 489 - 500 °F | Tubular (Blown) Film |
| 260 - 270 °C | 500 - 518 °F | Cast Film | |
| Moisture Content | 0.040 % | 0.040 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Deflection Temperature, | 50°C | ASTM D648 |
| Puncture Index | 400 gm/mil | ASTM D1306, MD |
| Puncture Strength | 990 g | ASTM D1306, MD |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3970H TPE, PP Overmold or Standalone use
- Osprey Metals HTN 2 Brazing Powder
- LG Chemical Lupoy 1300-03 Polycarbonate Resin
- SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer
- SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific)
- SABIC Innovative Plastics NORYL PX1007 PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer
- Trelleborg R395 Natural Rubber Polyisoprene
- Chi Mei Polylac® PA-765B ABS - Flame Retardant
- Arlon 51271R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved