Hippe PPS

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Unreinforced, Extruded
Manufacturer	Erhard Hippe KG
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hippe PPS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High hardness and stiffness, good abrasion resistance, low moisture absorption, favorable insulating features, low dielectric, high non-inflammability and high chemical resistance are the essential properties.Information provided by Hippe.

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	DIN 53 479
Water Absorption at Saturation	0.010 %	0.010 %	DIN 53 495

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	190 MPa @Time 30.0 sec	27600 psi @Time 0.00833 hour	DIN 53 456
Elongation at Break	20 %	20 %	DIN 53 455
Tensile Modulus	4.00 GPa	580 ksi	DIN 53 457
Flexural Modulus	4.20 GPa	609 ksi	from bending test; DIN 53 457
Charpy Impact, Notched	NB	NB	DIN 53 453
Tear Strength Test	80	80	in MPa; DIN 53 455

Thermal Properties	Metric	English	Comments
CTE, linear	50.0 µm/m-°C	27.8 µin/in-°F
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F
Melting Point	280 °C	536 °F	DIN 53 736
Maximum Service Temperature, Air	230 °C	446 °F	Continuous use
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F	ISO-R 75 Method A
Glass Transition Temp, Tg	88.0 °C	190 °F	dynamic; DIN 53 736
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.50e+16 ohm-cm	4.50e+16 ohm-cm	DIN 53 482, VDE 0303, Part 3
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	DIN 53 482
Dielectric Strength	21.0 kV/mm	533 kV/in	Breakdown; DIN 53 481, IEC-243, VDE 0303 Part 1
Dielectric Loss Index	0.0013 @Frequency 1.00e+6 Hz	0.0013 @Frequency 1.00e+6 Hz	DIN 53 483, IEC-250

Descriptive Properties	Value	Comments
Color	beige
Resistance to hot water, suds	resistant