Industeel SIRIUS 800 H+ Heat Resistant Alloy
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Groupe Arcelor |
| Trade Name | SIRIUS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel SIRIUS 800 H+ Heat Resistant Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: The SIRIUS® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUS® 800 is employed at temperature below 600°C(1112°F) while SIRIUS® 800H and SIRIUS® 800H+ are used above 600°C (1112°F). CLI heats obtained by vacuum degassing process have a tight control of the chemical analysis including residual elements in order to improve the weldability and in-service properties.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.00 g/cc | 0.289 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | Minimum Guaranteed |
| Tensile Strength, Yield | >= 170 MPa @Strain 0.200 % |
>= 24700 psi @Strain 0.200 % |
|
| Elongation at Break | >= 35 % | >= 35 % | |
| Creep Strength | 140 MPa @Temperature 600 °C, Time 3.60e+7 sec |
20300 psi @Temperature 1110 °F, Time 10000 hour |
1% elongation |
| Modulus of Elasticity | 196 GPa | 28400 ksi | |
| Poissons Ratio | 0.342 | 0.342 | Calculated |
| Shear Modulus | 73.0 GPa @Temperature 20.0 °C |
10600 ksi @Temperature 68.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.5 µm/m-°C @Temperature 0.000 - 100 °C |
7.50 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 14.5 µm/m-°C @Temperature 0.000 - 100 °C |
8.06 µin/in-°F @Temperature 32.0 - 212 °F |
||
| 15.5 µm/m-°C @Temperature 0.000 - 400 °C |
8.61 µin/in-°F @Temperature 32.0 - 752 °F |
||
| 17.0 µm/m-°C @Temperature 0.000 - 600 °C |
9.44 µin/in-°F @Temperature 32.0 - 1110 °F |
||
| Specific Heat Capacity | 0.502 J/g-°C @Temperature 20.0 °C |
0.120 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 13.0 W/m-K @Temperature 20.0 °C |
90.2 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Annealing Point | 1150 °C | 2100 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.060 - 0.10 % | 0.060 - 0.10 % | |
| Chromium, Cr | 19 - 23 % | 19 - 23 % | |
| Copper, Cu | <= 0.75 % | <= 0.75 % | |
| Iron, Fe | 38.925 - 50.09 % | 38.925 - 50.09 % | As remainder |
| Nickel, Ni | 30 - 35 % | 30 - 35 % | |
| Phosphorous, P | <= 0.020 % | <= 0.020 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.0050 % | <= 0.0050 % | |
| Ti + Al | 0.85 - 1.2 % | 0.85 - 1.2 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000100 ohm-cm @Temperature 20.0 °C |
0.000100 ohm-cm @Temperature 68.0 °F |
Users viewing this material also viewed the following:
- Momentive Performance Materials IS803 Black Adhesive Sealant, General Purpose Paste
- Solvay Specialty Polymers Hyflon® PFA P455 Perfluoroalkoxy (PFA)
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- Lubrizol ESTANE® 58226 Ester Based Thermoplastic Polyurethane
- A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene
- Eagle Brass 19210 XP-10 Copper Iron, Spring
- DSM Stanyl® TS250F4D Nylon 46-40% Glass Reinforced (Asian Grade) (Cond)
- 3M SJ6553 Protective Product, Molded Shapes
- DSM Akulon® F223-DH Nylon 6 (European Grade) (Cond) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved