Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber

Category	Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer	Hexcel
Trade Name	HexPly®
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Information provided by HexCel

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³	Resin Density
	2.56 g/cc	0.0925 lb/in³	Fibre Density

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi	90º, RT, Dry; EN2561
	1560 MPa	226000 psi	RT; Dry; EN2561
	16.0 MPa <br>@Temperature 100 °C	2320 psi <br>@Temperature 212 °F	90º, Wet; EN2561
	23.0 MPa <br>@Temperature 75.0 °C	3340 psi <br>@Temperature 167 °F	90º, Wet; EN2561
	620 MPa <br>@Temperature 100 °C	89900 psi <br>@Temperature 212 °F	Wet; EN2561
	670 MPa <br>@Temperature 75.0 °C	97200 psi <br>@Temperature 167 °F	Wet; EN2561
Tensile Modulus	16.0 GPa	2320 ksi	90º, RT, Dry; EN2561
	56.0 GPa	8120 ksi	RT; Dry; EN2561
	8.00 GPa <br>@Temperature 100 °C	1160 ksi <br>@Temperature 212 °F	90º, Wet; EN2561
	11.0 GPa <br>@Temperature 75.0 °C	1600 ksi <br>@Temperature 167 °F	90º, Wet; EN2561
	50.0 GPa <br>@Temperature 100 °C	7250 ksi <br>@Temperature 212 °F	Wet; EN2561
	51.0 GPa <br>@Temperature 75.0 °C	7400 ksi <br>@Temperature 167 °F	Wet; EN2561
Compressive Yield Strength	130 MPa	18900 psi	RT; Dry; DIN65380
	214 MPa	31000 psi	90º, RT, Dry; DIN65380
	140 MPa <br>@Temperature 100 °C	20300 psi <br>@Temperature 212 °F	90º, Wet; DIN65380
	165 MPa <br>@Temperature 75.0 °C	23900 psi <br>@Temperature 167 °F	90º, Wet; DIN65380
	800 MPa <br>@Temperature 100 °C	116000 psi <br>@Temperature 212 °F	Wet; DIN65380
	850 MPa <br>@Temperature 75.0 °C	123000 psi <br>@Temperature 167 °F	Wet; DIN65380
Compressive Modulus	16.5 GPa	2390 ksi	90º, RT, Dry; DIN65380
	58.0 GPa	8410 ksi	RT; Dry; DIN65380
	12.0 GPa <br>@Temperature 100 °C	1740 ksi <br>@Temperature 212 °F	90º, Wet; DIN65380
	13.5 GPa <br>@Temperature 75.0 °C	1960 ksi <br>@Temperature 167 °F	90º, Wet; DIN65380
	52.0 GPa <br>@Temperature 100 °C	7540 ksi <br>@Temperature 212 °F	Wet; DIN65380
	53.0 GPa <br>@Temperature 75.0 °C	7690 ksi <br>@Temperature 167 °F	Wet; DIN65380
Shear Strength	67.0 MPa	9720 psi	In-Plane, RT, Dry; EN6031
	95.0 MPa	13800 psi	0º, ILSS (Short Beam), RT, Dry; EN2563
	45.0 MPa <br>@Temperature 100 °C	6530 psi <br>@Temperature 212 °F	0º, ILSS (Short Beam), Wet; EN2563
	45.0 MPa <br>@Temperature 100 °C	6530 psi <br>@Temperature 212 °F	In-Plane, Wet; EN6031
	52.0 MPa <br>@Temperature 75.0 °C	7540 psi <br>@Temperature 167 °F	In-Plane, Wet; EN6031
	61.0 MPa <br>@Temperature 75.0 °C	8850 psi <br>@Temperature 167 °F	0º, ILSS (Short Beam), Wet; EN2563

Processing Properties	Metric	English	Comments
Shelf Life	14.0 Month <br>@Temperature -18.0 °C	14.0 Month <br>@Temperature -0.400 °F

Descriptive Properties	Value	Comments
Cured Thickness per Ply (cm)	0.25
Fiber Volume (%)	60