SABIC Innovative Plastics LNP THERMOCOMP 9X07435
| Category | Polymer , Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X07435.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* is a compound based on Miscellaneous resin containing Proprietary Filler(s). Added feature of this grade is: Plateable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
| 59.0 MPa | 8560 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 | |
| 2.2 % | 2.2 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.81 GPa | 698 ksi | 1 mm/min; ISO 527 |
| 5.45 GPa | 790 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
| 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.01 GPa | 727 ksi | 2 mm/min; ISO 178 |
| 5.35 GPa | 776 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.72 J/cm | 5.10 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1.00e+9 Hz |
2.9 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.0046 @Frequency 1.00e+9 Hz |
0.0046 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Nanocyl EPOCYL™ NC R1MY-04 Master Batch Liquid tetrafunctional epoxy Resin for solvent based Formulation Purposes: Dilution Factor 6
- Honeywell Capran® 512 LL Heat Stabilized Nylon Film (discontinued **)
- Flint Hills P5M6K-080 Polypropylene Random Copolymer
- Möller Medical TafSkin 115 NanoCoating
- Lucent Polymers PC/PBT-1550 Polycarbonate+PBT, Improved Impact Resistance, Injection Grade
- Sylvin Technologies 9999-60 Natural PVC Molding Compound
- Solvay Technyl® C216V15 15% Glass Filled Nylon 6
- Von Roll Isola IMI Varnish 716 Solventless Polyester Varnish for Electrical Insulation
- Clariant Renol ABS3470 ABS, High Heat, Low Gloss
Copyright © lookpolymers.com All Rights Reserved