Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of high-temperature.
Physical Properties Metric English Comments
Density 8.44 g/cc
0.305 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 915 MPa
133000 psi
Tensile Strength, Yield 425 MPa

@Strain 0.200 %
 61600 psi

@Strain 0.200 %
Elongation at Break 46 %
46 %
in 50.8 mm
Modulus of Elasticity 208 GPa
30200 ksi
RT
126 GPa

@Temperature 1000 °C
 18300 ksi

@Temperature 1830 °F
142 GPa

@Temperature 900 °C
 20600 ksi

@Temperature 1650 °F
153 GPa

@Temperature 800 °C
 22200 ksi

@Temperature 1470 °F
163 GPa

@Temperature 700 °C
 23600 ksi

@Temperature 1290 °F
171 GPa

@Temperature 600 °C
 24800 ksi

@Temperature 1110 °F
179 GPa

@Temperature 500 °C
 26000 ksi

@Temperature 932 °F
186 GPa

@Temperature 400 °C
 27000 ksi

@Temperature 752 °F
192 GPa

@Temperature 300 °C
 27800 ksi

@Temperature 572 °F
199 GPa

@Temperature 200 °C
 28900 ksi

@Temperature 392 °F
201 GPa

@Temperature 100 °C
 29200 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 12.8 µm/m-°C

@Temperature 25.0 - 100 °C
 7.11 µin/in-°F

@Temperature 77.0 - 212 °F
13.1 µm/m-°C

@Temperature 25.0 - 200 °C
 7.28 µin/in-°F

@Temperature 77.0 - 392 °F
13.4 µm/m-°C

@Temperature 25.0 - 300 °C
 7.44 µin/in-°F

@Temperature 77.0 - 572 °F
13.8 µm/m-°C

@Temperature 25.0 - 400 °C
 7.67 µin/in-°F

@Temperature 77.0 - 752 °F
14.2 µm/m-°C

@Temperature 25.0 - 500 °C
 7.89 µin/in-°F

@Temperature 77.0 - 932 °F
14.8 µm/m-°C

@Temperature 25.0 - 600 °C
 8.22 µin/in-°F

@Temperature 77.0 - 1110 °F
15.4 µm/m-°C

@Temperature 25.0 - 700 °C
 8.56 µin/in-°F

@Temperature 77.0 - 1290 °F
16.0 µm/m-°C

@Temperature 25.0 - 800 °C
 8.89 µin/in-°F

@Temperature 77.0 - 1470 °F
16.7 µm/m-°C

@Temperature 25.0 - 900 °C
 9.28 µin/in-°F

@Temperature 77.0 - 1650 °F
17.4 µm/m-°C

@Temperature 25.0 - 1000 °C
 9.67 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.410 J/g-°C
0.0980 BTU/lb-°F
RT
0.428 J/g-°C

@Temperature 100 °C
 0.102 BTU/lb-°F

@Temperature 212 °F
0.455 J/g-°C

@Temperature 200 °C
 0.109 BTU/lb-°F

@Temperature 392 °F
0.477 J/g-°C

@Temperature 300 °C
 0.114 BTU/lb-°F

@Temperature 572 °F
0.503 J/g-°C

@Temperature 400 °C
 0.120 BTU/lb-°F

@Temperature 752 °F
0.527 J/g-°C

@Temperature 500 °C
 0.126 BTU/lb-°F

@Temperature 932 °F
0.552 J/g-°C

@Temperature 600 °C
 0.132 BTU/lb-°F

@Temperature 1110 °F
0.576 J/g-°C

@Temperature 700 °C
 0.138 BTU/lb-°F

@Temperature 1290 °F
0.600 J/g-°C

@Temperature 800 °C
 0.143 BTU/lb-°F

@Temperature 1470 °F
0.625 J/g-°C

@Temperature 900 °C
 0.149 BTU/lb-°F

@Temperature 1650 °F
0.648 J/g-°C

@Temperature 1000 °C
 0.155 BTU/lb-°F

@Temperature 1830 °F
Thermal Conductivity 9.80 W/m-K
68.0 BTU-in/hr-ft²-°F
RT
10.9 W/m-K

@Temperature 100 °C
 75.6 BTU-in/hr-ft²-°F

@Temperature 212 °F
12.5 W/m-K

@Temperature 200 °C
 86.8 BTU-in/hr-ft²-°F

@Temperature 392 °F
13.9 W/m-K

@Temperature 300 °C
 96.5 BTU-in/hr-ft²-°F

@Temperature 572 °F
15.3 W/m-K

@Temperature 400 °C
 106 BTU-in/hr-ft²-°F

@Temperature 752 °F
16.9 W/m-K

@Temperature 500 °C
 117 BTU-in/hr-ft²-°F

@Temperature 932 °F
18.3 W/m-K

@Temperature 600 °C
 127 BTU-in/hr-ft²-°F

@Temperature 1110 °F
19.8 W/m-K

@Temperature 700 °C
 137 BTU-in/hr-ft²-°F

@Temperature 1290 °F
21.5 W/m-K

@Temperature 800 °C
 149 BTU-in/hr-ft²-°F

@Temperature 1470 °F
23.4 W/m-K

@Temperature 900 °C
 162 BTU-in/hr-ft²-°F

@Temperature 1650 °F
25.6 W/m-K

@Temperature 1000 °C
 178 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1290 - 1350 °C
2350 - 2460 °F
Solidus 1290 °C
2350 °F
Liquidus 1350 °C
2460 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.40 %
<= 0.40 %
Carbon, C <= 0.10 %
<= 0.10 %
Chromium, Cr 21 %
21 %
Cobalt, Co <= 1.0 %
<= 1.0 %
Iron, Fe <= 5.0 %
<= 5.0 %
Manganese, Mn <= 0.50 %
<= 0.50 %
Molybdenum, Mo 9.0 %
9.0 %
Nickel, Ni 62 %
62 %
As Remainder
Niobium, Nb (Columbium, Cb) 3.7 %
3.7 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000129 ohm-cm
0.000129 ohm-cm
RT
0.000132 ohm-cm

@Temperature 100 °C
 0.000132 ohm-cm

@Temperature 212 °F
0.000134 ohm-cm

@Temperature 200 °C
 0.000134 ohm-cm

@Temperature 392 °F
0.000135 ohm-cm

@Temperature 300 °C
 0.000135 ohm-cm

@Temperature 572 °F
0.000135 ohm-cm

@Temperature 1000 °C
 0.000135 ohm-cm

@Temperature 1830 °F
0.000136 ohm-cm

@Temperature 900 °C
 0.000136 ohm-cm

@Temperature 1650 °F
0.000136 ohm-cm

@Temperature 400 °C
 0.000136 ohm-cm

@Temperature 752 °F
0.000137 ohm-cm

@Temperature 500 °C
 0.000137 ohm-cm

@Temperature 932 °F
0.000137 ohm-cm

@Temperature 800 °C
 0.000137 ohm-cm

@Temperature 1470 °F
0.000138 ohm-cm

@Temperature 600 °C
 0.000138 ohm-cm

@Temperature 1110 °F
0.000138 ohm-cm

@Temperature 700 °C
 0.000138 ohm-cm

@Temperature 1290 °F