- Grupo Repol Dinalon® A1S25 G30XV0 PA66 30% Glass Fiber V0
Grupo Repol Dinalon® A1S25 G30XV0 PA66 30% Glass Fiber V0
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® A1S25 G30XV0 PA66 30% Glass Fiber V0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75/A |
| Vicat Softening Point | >= 230 °C | >= 446 °F | 50N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C | 1760 °F | UNE-EN 60695 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SA300S20 Silver-coated Aluminum Granules
- Premix Thermoplastics PRE-ELEC® PP 1378
- Lucite International Lucite® 1192 Glass Separation Resin
- Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure
- SABIC Innovative Plastics LNP THERMOCOMP DX07350 PC (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-LOY KX01002 Acetal Copolymer (Europe-Africa-Middle East)
- Axiall 8916 Moldings & Extrusions Flexible PVC
- Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound (discontinued **)
- Hexcel® HexPly® M65 Bismaleimide Resin
Copyright © lookpolymers.com All Rights Reserved