Gromax CFG30-QN11N1 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax CFG30-QN11N1 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 163 MPa | 23600 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 3.6 % | 3.6 % | 50 mm/min; ISO 527 |
| Flexural Strength | 246 MPa | 35700 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.04 GPa | 1170 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.7 kJ/m² | 6.99 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 280 °C | 511 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Covestro Petlon® DP3-1039 Semi-Crystalline PET, 35% Glass Fiber (discontinued **)
- Eastman CM01 PET (discontinued **)
- PolyOne Nymax™ GF 1880 33 HS NATURAL Nylon 6/12, Glass Filled (discontinued **)
- Styron DL 2241LA Carboxylated SB
- Styron DL 447 SB Latex
- Universal Wire Works 901 (AMS 5660) Nickel Alloy Filler Metal
- Eurostar Starglas FX05032 PE
- Beijing Chemical Industry KAIFA® GL6000 ABS Metal Plating Grade
- Bostik 1525 Medium Performance, Oil Resistant Polyamide Glue Stick
- Hexcel® HexWeb® CR III 1/8-5052-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved