Gromax BFG10-BN00N1 Nylon 6 10% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG10-BN00N1 Nylon 6 10% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ISO 1183 |
| Moisture Absorption | 1.20 % | 1.20 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Temperature 80.0 °C |
0.0050 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Temperature 80.0 °C |
0.0090 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 98.1 MPa | 14200 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 4.90 GPa | 711 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 155 MPa | 22500 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 3.43 GPa | 498 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.540 J/cm² @Temperature 23.0 °C |
2.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- OMG Americas GlidCop® AL-60 Dispersion Strengthened Copper
- Polykemi AB POLYfill PP EIP16020 F PP Mineral Reinforced, Extrusion Grade, Low CLTE
- Arlon A3020-R008-16.5 0.020" (0.508 mm) Cured Fusible Silicone Rubber with Sinusoidal Fiberglass Substrate &nb
- SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP VERTON MV006SU PP (Asia Pacific)
- Unipetrol Medium Stabilized Oil Hydrogenate
- A. Schulman POLYBATCH™ XAMF-500-T Process Aid Concentrate, Concentrate Based In LLDPE
- PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-214-S(HT) Powdered Metal
- Bhansali Engineering Santron IMS1000 Sparkle SAN Resin
Copyright © lookpolymers.com All Rights Reserved