- SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East)
SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Post-industrial recycle based, 30% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C |
0.40 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 19 g/10 min @Load 5.00 kg, Temperature 360 °C |
19 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature 23.0 - 150 °C |
10.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature 23.0 - 150 °C |
32.2 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 188 °C | 370 °F | Rate B/50; ISO 306 |
| 195 °C | 383 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Quadrant EPP Fluorosint® MT-01 Proprietary fluoropolymer reinforced with carbon fibers and organometallic fillers( ASTM Product Data Sheet)
- Teknor Apex Sarlink® 4145 Thermoplastic Elastomer
- Master Bond MB297MED Cyanoacrylate Biocompatible Adhesive System
- Diamond Polymers DIAMALOY 761 ABS/PC Alloy, Non-Halogen Flame Retardant with 5% PTFE
- Dow Nordel® IP 4520 Molded Golf Grip
- BASF Neopolen® P 9435 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- Eastman D4052-F Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved