Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.0074 - 0.0076 cm/cm @Thickness 3.20 mm |
0.0074 - 0.0076 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 36.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
36.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Melt Index of Compound | 35 g/10 min @Load 1.20 kg, Temperature 300 °C |
35 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 | |
Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
Elongation at Break | 47.9 % | 47.9 % | 5 mm/min; ISO 527 |
59 % | 59 % | Type I, 5 mm/min; ASTM D638 | |
Elongation at Yield | 5.4 % | 5.4 % | Type I, 5 mm/min; ASTM D638 |
5.4 % | 5.4 % | 5 mm/min; ISO 527 | |
Tensile Modulus | 2.59 GPa | 376 ksi | 5 mm/min; ASTM D638 |
Flexural Yield Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Izod Impact, Notched | 5.47 J/cm | 10.2 ft-lb/in | ASTM D256 |
1.59 J/cm @Temperature -30.0 °C |
2.98 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1A |
15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
Charpy Impact, Notched | 3.40 J/cm² | 16.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
68.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
CTE, linear, Transverse to Flow | 68.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
68.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ASTM D1525 |
144 °C | 291 °F | Rate B/50; ISO 306 | |
146 °C | 295 °F | Rate B/120; ISO 306 |