Garlock 706 Compressed Inorganic Fiber Gasketing, Nitrile Binder

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Garlock Rubber Technologies
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Garlock 706 Compressed Inorganic Fiber Gasketing, Nitrile Binder.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Inorganic fibers with a nitrile binder.Inorganic, asbestos-free fibers offer superior performance in saturated and superheated steamThermally stable fibers retain effective seal even during thermal cycling to 750Â°F (400Â°C)Unique manufacturing process minimizes cold flow and creep relaxation problemsIdeal for standard ANSI flanged connectors, as well as turbine crossover piping connectorsMultiple applications in power generation, chemical processing, hydrocarbon processing, and other industriesMedia: Steam, oils, grease, water, heat transfer fluidsInformation provided by Garlock Rubber Technologies

Physical Properties	Metric	English	Comments
Density	1.68 g/cc	0.0608 lb/inÂ³

Mechanical Properties	Metric	English	Comments
Tensile Strength	9.65 MPa	1400 psi	across grain; ASTM F152

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	538 Â°C	1000 Â°F
	399 Â°C @Pressure 10.3 MPa	750 Â°F @Pressure 1500 psi	Continuous
Minimum Service Temperature, Air	-73.3 Â°C	-100 Â°F

Electrical Properties	Metric	English	Comments
Dielectric Strength	0.984 kV/mm	25.0 kV/in	100% RH for 96 hours; ASTM D149
	5.24 kV/mm @Temperature 121 Â°C, Time 10800 sec	133 kV/in @Temperature 250 Â°F, Time 3.00 hour	0.0625 in. thickness; ASTM D149
	5.59 kV/mm @Temperature 121 Â°C, Time 10800 sec	142 kV/in @Temperature 250 Â°F, Time 3.00 hour	0.125 in. thickness; ASTM D149

Descriptive Properties	Value	Comments
Color	White
Compressibility, %	7-17	ASTM F36
Creep Relaxation, %	18	ASTM F38
Sealability ASTM F37B, ml/hr	0.5	ASTM Fuel A
	4	Nitrogen