Loxim 820 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 820 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 - 1.10 g/cc | 1.00 - 1.10 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.013 - 0.015 cm/cm | 0.013 - 0.015 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 - 32.0 MPa | 4350 - 4640 psi | ASTM D683 |
| Flexural Modulus | 2.00 - 2.20 GPa | 290 - 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 - 0.400 J/cm | 0.562 - 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 - 120 °C | 230 - 248 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Raschig Group 4554 Silicone
- Nilit Nilamid A3 H6 G5 25% Glass Reinforced PA66
- LG Chemical GPPS 25SP(E) PS, High Transparency, Heat Resistance
- Lubriplate AC-2 Petroleum-Based Air Compressor Fluid
- Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber
- Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes
- Sinotek Materials ZSKP50 Ultra Low Sulfur Expandable Graphite
- Total PPH 5069 Polypropylene Homopolymer, Fiber
- A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene
- Dymax 9-20526 HGA and OHGA Disk Drive Adhesive
Copyright © lookpolymers.com All Rights Reserved