Toyobo PELPRENE™ S6002 Polyester TPE, Ultra Heat-resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ S6002 Polyester TPE, Ultra Heat-resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Ultra Heat-resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.017 cm/cm @Thickness 2.00 mm |
0.017 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 8.0 g/10 min @Temperature 230 °C |
8.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 99 | 99 | JIS K6301 |
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 450 % | 450 % | ASTM D638 |
| 50% Modulus | 0.0275 GPa | 3.99 ksi | ASTM D638 |
| Flexural Modulus | 0.568 GPa | 82.4 ksi | ASTM D790 |
| Compressive Modulus | 0.0308 GPa | 4.47 ksi | 0.1; ASTM D695 |
| Resilience | 56 | 56 | JIS K6301 |
| Izod Impact, Notched | 1.96 J/cm | 3.67 ft-lb/in | ASTM D256 |
| Tear Strength | 196 kN/m | 1120 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 218 °C | 424 °F | By DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 202 °C | 396 °F | ASTM D1525 |
| Brittleness Temperature | -60.0 °C | -76.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+14 ohm-cm | 5.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1985T TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Asia Pacific)
- PTS PCA-2201NHV Non Bromine, Non Chlorine Flame Retardant Polycarbonate/ABS Alloy, UV Stabilized
- PolyMirae Moplen EP340K Sheet and Thermoforming Grade Polypropylene
- Ineos ABS Lustran® 1460, Injection Grade (discontinued **)
- PolyOne Edgetek® PE-30MC-20TC/000 High Density Polyethylene (HDPE), Talc Filled (discontinued **)
- Shandong Dongyue Shenzhou New Material Co CHFM 050 Perfluorosulfonic Acid Proton Exchange Membrane (PFSAPEM)
- Epoxy Technology EPO-TEK® H20E-8 Electrically Conductive, Silver Epoxy
Copyright © lookpolymers.com All Rights Reserved