Firestone C212-15C Nylon 6, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized |
| Manufacturer | Firestone |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Firestone C212-15C Nylon 6, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Off white color. Heat stabilized, Modified, and Lubricated. Chip size is 2 x 3.5 mm.Information provided by Firestone
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Viscosity Measurement | 3.2 | 3.2 | Relative Viscosity; Sulfuric Acid |
| 82 | 82 | Relative Viscosity; Formic Acid |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 79.2 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D412 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | |
| Melt Temperature | 249 - 260 °C | 480 - 500 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W3400 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Braskem ES 300 HDPE Blown Film Extrusion Polyethylene (discontinued **)
- Michelman® Mold Release 225SS Synthetic wax emulsion
- SABIC Innovative Plastics Ultem ATX153R PEI+PCE
- Unifrax Fiberfrax® Washed 757 High Purity High-Index Fiber
- Zeon Chemicals Zeonex® 480 Cyclo-Olefin Polymer
- Ensinger TECASINT™ 2031 Polyimide, 40% Graphite Filled (PI)
- 3M AC-665 Class C-48 Aerospace Sealant
- PolyOne Edgetek® AT-30GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved