- Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate
Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 6.35 mm |
0.011 in/in @Thickness 0.250 in |
ASTM D955 |
| 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 | |
| Melt Flow | 13 g/10 min | 13 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Strength | 44.1 MPa | 6400 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Enviramid™ N1300STHL Post Consumer Recycle Nylon 66
- NOVA Chemicals Novapol® TR-0535-UIG Hexene MDPE Rotational Molding Resin
- Solvay Specialty Polymers Halar® 500 ECTFE Fluoropolymer (discontinued **)
- Eastman Tenite 358-10 Cellulose Acetate Propionate (discontinued **)
- Hyosung Topilene J340 PP
- Kobe Steel Titanium alloy with low alloying elements, ASTM Gr. 7, Annealed
- LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic
- Daelim H&L Plavis-G15 DF 15% Graphite Filled Aromatic Polyimide Bearing
- Monmouth Rubber & Plastics Durafoam™ P192HD EPDM
Copyright © lookpolymers.com All Rights Reserved