- Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
- PolyOne Edgetek® LC-30GF/000 LCP (Liquid Crystal Polymer), 30% Glass Reinforced, Hi-Temp (discontinued **)<
PolyOne Edgetek® LC-30GF/000 LCP (Liquid Crystal Polymer), 30% Glass Reinforced, Hi-Temp (discontinued **)<
| Category | Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® LC-30GF/000 LCP (Liquid Crystal Polymer), 30% Glass Reinforced, Hi-Temp
(discontinued **)<.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne™ Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Thickness 3.17 mm |
0.020 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 159 MPa | 23000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | Method A, Injection Molded, 0.125 in bars, 73°F; ASTM D648 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 470 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Processing Method | Injection Molding |
Users viewing this material also viewed the following:
- Nabaltec ACTILOX® 200SM AlO(OH) Boehmite
- Haynes NS-163® Cobalt Alloy
- SABIC Innovative Plastics Ultem AUT230M PEI (Asia Pacific)
- Saint-Gobain Meldin® 5055 Thermoplastic Bearing Material
- American Polymers API 410 Polystyrene
- ChevronTexaco HDAX® ISO 100 NG Screw Compressor Oil
- Dow Corning SILASTIC® LS 5-8760 FLUOROSILICONE RUBBER
- ACC QM 140 QSI Quantum Silicones 40 Durometer Condensation Cured Moldmaking Material
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved