Polymer Property : Tensile Strength, Ultimate = 12.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PE 1294 PRE-ELEC PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 129..
Tensile Strength, Ultimate	12.0 MPa	1740 psi
3M Dyneon™ Fluorel™ FX-11818 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 68.6%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. 68.6% F grade terpolymer for difficul..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
ExxonMobil Optema® TC-020 Ethylene Methyl Acrylate for Injection Molding (discontinued **) Data provided by the manufacturer, Exxon Chemical.6.5% Methyl Acrylate. An Ethylene Methyl Acrylate copolymer which can be injection molded to produce pliable parts. It can also be used for making..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	500 mm/min (20 in./min.); Type IV Specimen; ASTM D638
Eastman 800E Polyethylene (discontinued **) Polyethylene 800E is used in general-purpose extrusion applications that also require good stress resistance. This formula complies with FDA regulations at 21 CFR177.1520 (c)(2.2) for use in articl..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman Voridian 800P Polyethylene (discontinued **) General purpose low density formulation used for extrusion coating applications that require good stress resistance. This formula complies with FDA regulations at 21 CFR 177.1520(c)(2.1) for use i..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1033 Film Extrusion Polyethylene (discontinued **) Homopolymer, and FDA compliant.Features: Good opticals, impact strength, good processing properties, and stiffnessApplications: Film extrusion: general purpose packaging and film applications.FDA No..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1080 Film Extrusion Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Yields film with high clarity and excellent stiffness.Applications: Film extrusion: overwrapFDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE7018 Profile Extrusion Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Excellent strength, good machinability, and foaming characteristics.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 17..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
ExxonMobil Escorene® LD-761 High EVA Compounding Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 28% vinyl acetate copolymer designed for high filler acceptance. Compounds produced from this resin have excellent flexibility and toughness.Appl..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
ExxonMobil Escorene® LD-769 High EVA Compounding Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 28% vinyl acetate copolymer designed for high filler acceptance. Compounds produced from this resin have excellent flexibility and toughness.Appl..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1356 EVA Film Extrusion (discontinued **) 3.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1903 EVA Film Extrusion (discontinued **) 9% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent toughness and flexibility at low temperatures, and good heat-seal response.Applications: Film extrusion: laminating film, controll..
Tensile Strength, Ultimate	12.0 MPa @Thickness 2.00 mm	1740 psi @Thickness 0.0787 in	ASTM D4894
3M Dyneon™ TFM™ 4212 Modified PTFE, 10% Electrocarbon Filled (discontinued **) Applications include bearings, seals/gaskets, packings, piston rings.Data provided by Dyneon.
Tensile Strength, Ultimate	12.0 MPa @Temperature 22.0 Â°C	1740 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® MMC 1600 Unsaturated Polyester UP MMC 1600 is a mineral moulding compound (similar to DMC/BMC) providing of a stone like appearance eg. granite or marble. Chrome plated mould surfaces are required. It is recommended that product thi..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D412
Multibase Multi-FlexÂ® TPE A 3104-10 AGATE 5ES The material is based on Kraton G rubber. It has been engineered for single shot. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
LyondellBasell Hifaxâ„¢ CA199AC Thermoplastic Olefin Resin Key Features: low melt flow, medium low modulus, paintable thermoplastic olefin resin, excellent balance of properties, high toughness, good paintability, flexibleApplications: automotive air bag do..
Tensile Strength, Ultimate	12.0 MPa @Temperature 49.0 °C	1740 psi @Temperature 120 °F	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 560 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	12.0 MPa	1740 psi
Dow DOWLEX™ IP-50 High Density Polyethylene DOWLEX® IP-50 resin is an improved processing high density polyethylene resin with controlled molecular weight distribution designed for thin wall food containers. This resin is recommended for flo..
Tensile Strength, Ultimate	12.0 - 30.0 MPa	1740 - 4350 psi
ATG s.r.l. IR Synthetic Polyisoprene
Tensile Strength, Ultimate	12.0 MPa @Temperature 250 °C	1740 psi @Temperature 482 °F	ASTM D638
Asahi Glass Fluon® P-805UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1078 Film Extrusion Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Yields film with high clarity and excellent stiffness.Applications: Film extrusion: overwrap packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1158 EVA Film Extrusion (discontinued **) 1.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE1335 EVA Film Extrusion (discontinued **) 3.3% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE 1375 EVA Film Extrusion (discontinued **) 3.7% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..
Tensile Strength, Ultimate	12.0 - 15.0 MPa	1740 - 2180 psi
Dow Advanta® 3302 Specialty Elastomer (discontinued **) Advanta® specialty elastomers provides good fluid resistance and better high temperature performance than nitrile or HNBR and lower cost than fluoroelastomers. Available in two grades. ASTM D2000..
Tensile Strength, Ultimate	12.0 - 15.0 MPa	1740 - 2180 psi
Dow Advanta® 3650 Specialty Elastomer (discontinued **) Advanta® specialty elastomers provides good fluid resistance and better high temperature performance than nitrile or HNBR and lower cost than fluoroelastomers. Available in two grades. ASTM D2000..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D412-80
DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerato..
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Huntsman PE6021 Blow Molding Polyethylene (discontinued **) Homopolymer, Drug Master File listed product, complies with USP Classification VI, and FDA compliant.Features: Meets exacting requirements of blow molded containers and processes well with parison s..