Eurotec® Tecotek® PC43 GR10 BK002 PC, 10% glass fiber reinforced, black
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecotek® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecotek® PC43 GR10 BK002 PC, 10% glass fiber reinforced, black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
| Vicat Softening Point | 145 °C @Load 5.10 kg |
293 °F @Load 11.2 lb |
ISO 306 |
| Glow Wire Test | 850 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
GWFI; IEC 60695 |
| 875 °C @Thickness 2.00 mm |
1610 °F @Thickness 0.0787 in |
GWIT; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Comparative Tracking Index | 175 V | 175 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 310 °C | 518 - 590 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | ISO 960 |
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Noble Polymers Regis™ 285107 Thermoplastic Olefin (TPO)
- Zircar Zirconia ZYP-30 Zirconia Powder
- Lotte Chemical Titan TITANPRO® SM240 Polypropylene impact copolymer
- SABIC Innovative Plastics Valox® 457 PBT (Europe-Africa-Middle East)
- ChevronTexaco Delo® Extended Life Coolant System, Coolant/Antifreeze
- ExxonMobil Bicor® 110 ASB-X OPP Film
- Aclo Accutech Polypropylene CP0437T40V Copolymer Talc Reinforced
- BASF Elastollan B 90 A TPUR
- DuPont Performance Polymers Zytel® BM70G20HSLX BK537 Nylon 66 (Unverified Data**)
- Resinlab® EP1305LV Black Epoxy Casting Resin
Copyright © lookpolymers.com All Rights Reserved