Eurotec® Tecotek® PC30 NL VB03 PC, unfilled, UV stabilized, high impact, natural
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified , Polycarbonate, UV Stabilized |
| Manufacturer | Eurotec |
| Trade Name | Tecotek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecotek® PC30 NL VB03 PC, unfilled, UV stabilized, high impact, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Tensile Modulus | 2.25 GPa | 326 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 |
| Vicat Softening Point | 125 °C @Load 5.10 kg |
257 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6/6 PA6/6 GR15 MF25 Glass/Mineral Filled Nylon
- Parker Chomerics THERM-A-FORM T642 Cure-in-Place Potting and Underfill Material
- Huntsman HZ 3365 Special Hardener
- Flint Hills P4C5N-046 Homopolymer Polypropylene
- Lubriplate SYN LUBE 68 PAO-Based Multi-Purpose Synthetic Fluid
- Sylvin Technologies 8940-95 Natural PVC Extrusion Compound
- Total PPC 7712 Polypropylene, Heterophasic Copolymer
- Cossa Polimeri ESTABLEND PA 1616 GF ABS / Nylon 6 Blend, 8% Glass Filled
- Axiall 9175 White 10 Rigid PVC, Molding, White 10
- Pyrotek LUMIFELT AL20L High Temperature Kevlar® Felt
Copyright © lookpolymers.com All Rights Reserved