- SABIC Innovative Plastics Cycolac® GX3800F ABS
SABIC Innovative Plastics Cycolac® GX3800F ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® GX3800F ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Viscosity | 1.40e+6 cP | 1.40e+6 cP | Melt Viscosity, 240°C, 100 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 31.6 % | 31.6 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.08 GPa | 302 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.32 J/cm | 8.09 ft-lb/in | ASTM D256 |
| 2.99 J/cm @Temperature -30.0 °C |
5.60 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 101 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 104 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 106 °C | 223 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Mallard Creek Polymers ROVENE® 4150 SBR Latex
- SABIC Innovative Plastics LNP LUBRICOMP IBP34 PA6.12
- Spartech Royalite R722 PVC Alloy Aircraft Grade Sheet
- SABIC Innovative Plastics LNP THERMOCOMP PX12419 PA 6
- A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66
- Polyram Polytron A60N01 Nylon 6.6, 60% Long Fiber Glass
- Axiall 22912 Coax & Telecom Flexible PVC
- Solvay TECHNYL® 1015CR PA6, Conditioned
- Lanxess Durethan® BKV 35 CX H2.0 900876 Nylon 6, Glass Fiber Reinforced
- Bulk Molding Compounds BMC T70 Automotive Grade Molding compound
Copyright © lookpolymers.com All Rights Reserved