- Eurotec® Tecodur® PB70 NL RT PBT, unfilled, PTFE modified, natural
Eurotec® Tecodur® PB70 NL RT PBT, unfilled, PTFE modified, natural
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), PTFE Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecodur® PB70 NL RT PBT, unfilled, PTFE modified, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Tensile Modulus | 2.75 GPa | 399 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 - 260 °C | 464 - 500 °F | |
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- RheTech Products FT2500-01A Thermoplastic Polyolefin, Non-UV Stabilized, Black
- PlastiComp Velocity® LCF50-PA6 High Flow Nylon 6, 50% Long Carbon Fiber
- Phillips Sumika Marlex® CHN-200 Thermoplastic Polyolefin (discontinued **)
- Overview of materials for Polycarbonate/Thermoplastic Polyurethane Blend
- Karina E TR 500D22/173 Honey PVC Compound
- DuPont Elvaloy® 2112 AC Ethylene and 12% Ethyl Acrylate Copolymer
- ExxonMobil Mobil Velocite 3
- LG Chemical NBR 6850 High Acrylonitrile Polymer
Copyright © lookpolymers.com All Rights Reserved