- Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0040 cm/cm @Thickness 6.35 mm |
0.0040 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 - 110 | 100 - 110 | ASTM D785 |
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | ASTM D638 |
| Flexural Strength | 107 MPa | 15500 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612 (Unverified Data**)
- Sylvin Technologies 9999-80 Natural PVC Molding Compound
- SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
- Dow Corning Z-6094 SILANE
- ACC MM709 Low Tear Condensation Cure 2-Part Molding Rubber
- Vyncolit Neopreg Kinel® SK4525 S5 Glass Fiber Reinforced Molding Compound
- Panjin Zhongrun Chemerize 085G Low Viscosity CoPEEK
- ExxonMobil Mobil Velocite 10
Copyright © lookpolymers.com All Rights Reserved