PolyOne Stat-Tech™ PI-30GF/15SS Polyetherimide (PEI), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ PI-30GF/15SS Polyetherimide (PEI), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Electrically ConductiveGlass Fiber ReinforcedStainless Steel Fiber FilledPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 152 MPa | 22000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 100 ohm-cm | 1.0 - 100 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.0 - 100 ohm | 1.0 - 100 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 371 - 410 °C | 700 - 770 °F | Molding |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® FG B3 Very Low Density Polyethylene
- Phillips 66 COPYLENE® CH200L Polypropylene, Homopolymer, CR, Antistat, Injection Molding
- Precision Polymer Engineering C60M Chloroprene Rubber
- A. Schulman POLYBATCH™ Silver 70100 Concentrate Based In LDPE
- Fainplast Compounds Ethylplus 621 HD Polyethylene Cable Compound
- Eurostar Starflam PZ00062E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Chi Mei Kibisan® PN-127H SAN
- Arlon LW3015B##-P0 0.030" (0.762 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Asahi Kasei Tenac®-C LD755 Copolymer Acetal Resin
- Dynasol Solprene® 9618 Multi-branched Thermoplastic Rubber (Multi-branched SBS)
Copyright © lookpolymers.com All Rights Reserved