- Eurotec® Tecodur® PB70 GR10 NL100 PBT, 10% glass fiber reinforced, natural
Eurotec® Tecodur® PB70 GR10 NL100 PBT, 10% glass fiber reinforced, natural
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecodur® PB70 GR10 NL100 PBT, 10% glass fiber reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 - 270 °C | 482 - 518 °F | |
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8911 (891-1) (UF) Synthetic Oil
- Polykemi AB POLYfill PPH TS4020D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant
- PolyOne Geon™ Vinyl Dry Blend E7364 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Chevron Phillips HiD® 9647T HDPE Blown Film Resin (discontinued **)
- Global PP-2300-NC Polypropylene Block Copolymer
- Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry)
- Hexcel® HexWeb® HRP - 3/16 - 4.0 Fiberglass/Phenolic Honeycomb
- ExxonMobil Mobil Centaur Moly 1
- Albis Plastics Cellulose Acetate Butyrate B9086 (FDA Odor Mask), 10% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved