- Eurostar Starpylen MX05038 TPEX, Injection Molded
Eurostar Starpylen MX05038 TPEX, Injection Molded
| Category | Polymer , Thermoplastic |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen MX05038 TPEX, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen MX05038 is a TPEX Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.3 % | 4.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.40 GPa | 203 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 28.0 MPa | 4060 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 105 kJ/m² | 50.0 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 109 µm/m-°C @Temperature 23.0 - 60.0 °C |
60.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 135 µm/m-°C @Temperature 23.0 - 60.0 °C |
75.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 240 - 250 °C | 464 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- RheTech Products HP520-01 12% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Black
- Reliance Industries PBT / PC - 35% Glass filled
- LG Chemical LUPOS HR2207A ABS+GF20%, General Purpose, Heat Resistance
- Momentive Performance Materials Zirconium Carbide (ZrC) Coating
- Karina 750-DM-48/1-B-IS Black PVC Compound
- Teknor Apex APEX® 155 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP Thermocomp RF0069 PA 66 (Europe-Africa-Middle East)
- Fainplast Compounds PG 58/1AT Flexible PVC, Extrusion Modified with Rubber
- BASF Ultradur B 4300 G2 LS High Speed BK15045 10% Glass Filled PBT
- Huntsman PE1201 EVA Film Extrusion (discontinued **)
Copyright © lookpolymers.com All Rights Reserved