- Eurostar Starpylen MFK42AS PP, Glass/Mineral Filled, Injection Molded
Eurostar Starpylen MFK42AS PP, Glass/Mineral Filled, Injection Molded
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen MFK42AS PP, Glass/Mineral Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen MFK42AS is a Mineral Filled, Glass Fiber Reinforced, Polypropylene Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % @Temperature 23.0 °C, Time 86400 sec |
0.020 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 4.00 mm |
0.0050 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.4 % | 5.4 % | Flexural, 5 mm/min; ISO 178 |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 37.0 MPa | 5370 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 51.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
28.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 116 µm/m-°C @Temperature 23.0 - 60.0 °C |
64.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 225 - 250 °C | 437 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer
- Nilit FRIANYL B63 D-S10 Nylon 6., std. viscosity for injection molding
- PolyMirae Moplen HP500G Sheet and Thermoforming Grade Polypropylene
- Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) (Unverified Data**)
- DAK Americas Laser+® C 9921 (F65A) PET
- Ashley Polymers Ashlene® T940H Nylon 11
- Saint-Gobain Chemfab® 1589 PTFE Coated Fiberglass Conveyor Belting
- Lubrizol Advanced Materials PEARLBOND® 521 Linear Thermoplastic Polyurethane
- ExxonMobil Santoprene® 111-45 Thermoplastic Elastomer
- BASF Ultramid® B3WG6 BK00564 BGVW 30% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved